抗静电聚甲醛(POM)的制备及其性能研究

时间:2020-01-14 20:39来源:毕业论文
采用简单的熔融共混法,将聚氨酯与离子液体共混,再将这一共混物与聚甲醛熔融复合,制得抗静电聚甲醛合金。并对材料的结构和性能进行了系统地研究

摘要聚甲醛是一个重要的工程塑料,具有优异的力学性能。然而,聚甲醛的韧性较差,同时难以满足抗静电要求。为此,在本文中,我们采用简单的熔融共混法,将聚氨酯与离子液体共混,再将这一共混物与聚甲醛熔融复合,制得抗静电聚甲醛合金。并对材料的结构和性能进行了系统研究。结果表明,当TPU/IL共混物的加入,聚甲醛的弹性模量和屈服模量下降了,断裂伸长率和抗静电性能明显提高了。尤其是当IL的含量达到4%时,其表面电阻和体积电阻分别为3.351010Ω  /‰和3.39109Ω • cm, ,具有优良的的抗静电效果。44007

Abstract: POM is an important engineering plastic with excellent mechanical properties. However, POM shows low toughness and bad anti-static properties. In this work, we have first blended polyurethane and ionic liquid to make a PU/IL blend, followed by simple melt the PU/IL blends with POM to fabricate the antistactic POM alloys. The morphology and properties of the prepared materials have been investigated. It was found that the elastic modulus and yield modulus of polyoxymethylene decrease, the elongation at break and the antistatic performance obviously improve with the addition of PU/IL blends. When the content of IL is 4%, its surface resistance is  3.351010Ω  /‰ ,and its volume resistance is3.39109Ω • cm ,which means excellent antistaic effect.

毕业论文关键词:聚甲醛; 聚氨酯; 离子液体;抗静电性:增韧

Keyword: POM;TPU; Ionic Liquids;Antistatic Behavior; Toughen 

目    录

1 绪论 1

1.1引言 1

1.2 聚甲醛及其共混改性介绍 1

1.2.1聚甲醛的发展及其现状 1

1.2.2聚甲醛的结构、性能及其应用 1

1.2.3聚甲醛改性的研究进展 1

1.3热塑性聚氨酯概述 1

1.3.1热塑性聚氨酯的发展及其现状 2

1.3.2热塑性聚氨酯的结构、性能及其应用 2

1.4离子液体在聚合物中的应用 2

1.4.1离子液体作为新型增塑剂在聚合物中的应用 2

1.4.2离子液体作为抗静电剂在聚合物中的应用 2

1.5本论文的研究思路、意义和主要内容 2

1.5.1本论文的研究思路及意义 2

1.5.2本论文的主要研究内容 2

2 实验部分 3

2.1 主要试剂 3

2.2 主要仪器设备 3

2.3 TPU/IL(SA-2)共混物制备 3

2.4 POM/(TPU/IL)共混物制备 3

2.5 实验表征和测试 4

3 结果与讨论 4

3.1 本研究实验策略的选择 4

3.2 TPU和IL的相容性表征 4

3.3 POM/(TPU/IL)共混物形貌结构的表征 5

3.3.1 POM/TPU共混物的形貌表征 5

3.3.2 POM/[(TPU/IL)]共混物形貌表征 6

3.4 POM/(TPU/IL)共混物聚集态结构的表征 抗静电聚甲醛(POM)的制备及其性能研究:http://www.lwfree.com/cailiao/lunwen_45148.html

------分隔线----------------------------
推荐内容